采用生物酶提高瓦楞原纸强度的研究 |
Pilot Enzymatic Treatment of Corrugating Medium |
|
DOI:10.11980/j.issn.0254-508X.2011.03.002 |
关键词: 漆酶 OCC浆 瓦楞原纸 环压指数 保水值 |
Key Words:laccase OCC pulp corrugating medium ring crush index WRV |
基金项目:本课题由以下项目提供资金支持:国家863项目(2007AA03Z433);广东省重点科技攻关项目(2008A030202008);广东省科技计划项目(2008B030302035)。 |
|
摘要点击次数: 5421 |
全文下载次数: 1627 |
摘要:采用漆酶-组氨酸的组合方式处理OCC浆,并先后在实验室和纸厂研究此生物处理方式对瓦楞原纸性能的影响。实验室小试研究结果表明,当漆酶和组氨酸的用量分别为0.90 U/g和1.0%(对绝干浆)时,成纸的干湿环压指数分别提高了22.9%和30.3%。中试结果也表明,漆酶和组氨酸用量分别为0.225 U/g和0.10%时,成纸干湿环压指数分别提高14.9%和26.4%,纵横向抗张指数分别提高8.0%和10.7%,耐破指数提高16.4%。同时生物处理在促进纤维分丝帚化方面也有明显效果,经处理的纤维保水值上升了40个百分点,纤维平均孔径和比表面积分别提高了1.1%和5.1%,并且浆料中羧基含量也提高了35.4%。 |
Abstract:In this paper, the influence of laccase-histidine on OCC fiber proterties was studied both in laboratory and mill. The laboratory results showed that when the amounts of laccase and histidine were 0.90 U/g and 1.0% respectively. The dry and wet ring crush index of papersheet increased by 22.9% and 30.3% compared with the control sample. Furthermore, the pilot test results also showed that when the amounts of laccase and histidine were 0.225 U/g and 0.10% (on oven dried pulp), the dry and wet ring crush index of papersheet increased by 14.9% and 26.4%, the longitudinal and cross tensile index increased by 8.0% and 10.7%, and brusting index increased by 16.4%, correspondingly. Besides, fibrillation was greatly developed and water retention value (WRV) increased by 37.5%. At the same time, the average pore size of fiber wall, specific surface area and carboxy group content increased by 1.1%, 5.1% and 35.4% respectively. |
查看全文 查看/发表评论 下载PDF阅读器 |