酸法制备芦苇微晶纤维素工艺的研究
Study on Reed MCC Preparation Process by Acid Hydrolysis
  
DOI:10.11980/j.issn.0254-508X.2015.01.015
关键词:  芦苇浆粕  微晶纤维素  酸水解
Key Words:reed pulp  MCC  acid hydrolysis
基金项目:
作者单位
韩 颖 大连工业大学,辽宁大连,116034 
李凤萍 大连工业大学,辽宁大连,116034 
樊婷婷 大连工业大学,辽宁大连,116034 
周景辉 大连工业大学,辽宁大连,116034 
郭延柱 大连工业大学,辽宁大连,116034 
摘要点击次数: 6783
全文下载次数: 1955
摘要:探讨以芦苇浆粕为原料制备芦苇微晶纤维素的可行性及工艺条件。用HCl为溶剂采用正交实验法对制备条件进行研究。结果表明,最佳制备工艺条件为:HCl质量分数6%,水解时间60 min,水解温度80℃,液比1∶10;其中水解温度的影响较大,水解产物聚合度(DP)为270.6 L/g,结晶度为73.2%,得率为85.4%;红外光谱和X射线能谱分析表明,所得产物为纤维素Ⅰ型,即微晶纤维素。
Abstract:The preparation conditions of microcrystalline cellulose (MCC) from reed pulp by using HCl as solvent were studied in this paper. By using orthogonal experiment method, study results showed that the optimal preparation conditions was HCl concentration 6%, hydrolysis time 60 min, temperature was 80℃, liquid ratio 1∶10. The temperature had larger impact on hydrolysis. Degree of polymerization (DP) of the product was 276.0 L/g, crystallinity was 73.2%, yield was 85.4%. The products were proved cellulose I (MCC) by infrared spectroscopy and X-ray spectroscopy characterization.