阳离子球形聚电解质刷的助留助滤性能 |
Performances of Cationic Spherical Polyelectrolyte Brushes Used as Retention and Drainage Aids |
|
DOI:10.11980/j.issn.0254-508X.2016.07.002 |
关键词: 助留助滤 CS-PDMC 填料 首程留着率 滤水速度 |
Key Words:retention and drainage properties CS-PDMC fillers retention rate filtration rate |
基金项目:国家自然科学基金资助项目(31170558)。 |
作者 | 单位 | 黄希妍1 | 1.武汉大学印刷与包装系,湖北武汉,430079 | 何宇航1 | 1.武汉大学印刷与包装系,湖北武汉,430079 | 郭 婷1 | 1.武汉大学印刷与包装系,湖北武汉,430079 | 黎厚斌1,* | 1.武汉大学印刷与包装系,湖北武汉,430079 | 袁世矩2 | 2.湖北工业大学,湖北武汉,430068 |
|
摘要点击次数: 6753 |
全文下载次数: 2197 |
摘要:制备了以碳球(CS)为核、甲基丙烯酰氧乙基三甲基氯化铵(DMC)为壳的阳离子球形聚电解质刷(CS-PDMC),探讨了其与阴离子聚丙烯酰胺(APAM)形成的二元体系中CS-PDMC用量对两种填料(重质碳酸钙(GCC)、高岭土)的首程留着率及浆料滤水性能的影响。当浆料中GCC用量15%时,加入用量0.8%的CS-PDMC(相对于绝干浆,以下同),GCC的首程留着率最高,为79.3%;当浆料中高岭土用量15%时,加入用量1.0%的CS-PDMC,高岭土的首程留着率最高,为88.5%。当浆料中GCC用量10%时,加入用量0.8%的CS-PDMC,浆料滤水速度最快,为0.91 mL/s;当浆料中高岭土用量5%时,加入用量0.8%的CS-PDMC,浆料的滤水速度最快,为0.83 mL/s。 |
Abstract:Cationic spherical polyelectrolyte brush has become new area of research as paper retention and drainage aids because of its structure characteristics.In this paper, the spherical polyelectrolyte brushes (CS-PDMC) with carbon spheres (CS) as core and methyl methacrylate three methyl ammonium chloride (DMC) as shell were prepared. The effects of different CS-PDMC dosageson the retention rates of two kinds of fillers (GCC, kaolin) and on the drainage of the furnishescontaining two kinds of fillers (GCC, kaolin) were studied. When 15% GCC(on the oven-dried pulp) and 0.8% CS-PDMC were added to the pulp, the retention rate of the filler was the highest for 79.3%; When 15% kaolin and 1.0% CS-PDMC were added to the pulp, the retention rate of the filler was the highest for 88.5%.When 10% GCC and 0.8% CS-PDMC were added to the pulp, the drainage rate was the fastest for 0.91 mL/s; when 5% kaolin and 0.8% CS-PDMC were added to the pulp, the drainage rate was the fastest for 0.83 mL/s. It indicated that using a certain amount of CS-PDMC was of benefit to the retention and drainage properties of the furnish containing the fillers. |